| P1005 Carbonized Fiber Packing Braided from shrink-proof oxdized polyacrylonitrile fiber impregnated with PTFE dispersion containing graphite particles,silicon-oil-free,Compared to traditional carbon fiber packing,it is not brittle,can suited for high peripheral speeds.It has highstrength and good thermal conductivity.PTFE and graphite mades the packing have excellent self-lubrication,so thes packing does not damage shafts and has long life. Carbonized Fiber Packing Reinforced with Nickel wire The wire reinforcement provides incerased mechanical strength,usually for static. Application:Used in weak acds and alkalis or media containing few grains of solid particles,both dynamic and static,mainly used for centrifugal pumps,plunger pumps,mixers and valves. carbonized fiber packing, carbon fiber packing |
|
Service Limits
|
| T |
280℃ |
| PH |
2-12 |
| V |
25m/s |
|
Rotating |
20bar |
| Reciprocating |
110bar |
| Valve |
200bar |
| g/cm³ |
1.4
|
|
| SWP805A Carbon Fiber packing |
| P1005A Carbon Fiber packing Braided from strong carbon contimuous yarns after softening,impregnated with proprietary lubricants and graphite partickes,which fill woids,act as a break-in lubricant,and block leakage. Carbon Fiber Packing Reinforced with Nickel wire The wire reinforcement provides increased mechanical strength,usually for static. Application:Used for pumps or valves in high pressure and high temperature.Handle water,steam,acids and aldalis for power stations,refineries,boiler plants etc. SWP805A is commonly used in steam turbines,high temperature motor-actuated valves and for high pressure,hignh temperature valve application in general. carbonized fiber packing, carbon fiber packing |
| Service Limits |
| T |
600℃ |
| PH |
2-12 |
| V |
20m/s |
| |
Rotating |
25bar |
| Reciprocating |
110bar |
| Valve |
200bar |
|
g/cm³
|
1.4
|
|